Thermal compatibility evaluation of veneering ceramic over zirconia : Evaluation of Thermal Compatibility of VITA VM 9 Veneering Ceramic Over VITA In-Ceram Zirconia Framework
5 Angebote vergleichen

Bester Preis: Fr. 43.12 ( 43.95)¹ (vom 01.07.2017)
1
9783330967465 - Fatien Fadilaldin: Thermal compatibility evaluation of veneering ceramic over zirconia : Evaluation of Thermal Compatibility of VITA VM 9 Veneering Ceramic Over VITA In-Ceram Zirconia Framework
Symbolbild
Fatien Fadilaldin

Thermal compatibility evaluation of veneering ceramic over zirconia : Evaluation of Thermal Compatibility of VITA VM 9 Veneering Ceramic Over VITA In-Ceram Zirconia Framework (2017)

Lieferung erfolgt aus/von: Deutschland DE PB NW

ISBN: 9783330967465 bzw. 3330967463, in Deutsch, Noor Publishing Jun 2017, Taschenbuch, neu.

Fr. 48.96 ( 49.90)¹
versandkostenfrei, unverbindlich
Lieferung aus: Deutschland, Versandkostenfrei.
Von Händler/Antiquariat, AHA-BUCH GmbH [51283250], Einbeck, Germany.
Neuware - The residual stresses generated during manufacturing of zirconia prostheses is the origin of unstable chipping observed clinically. The aim of this study was to analyzing the influence of porcelain thickness and the implemented cooling protocol on the magnitude of the developed residual stresses. 60 rectangular bilayered plates and thermal shock test were used to investigate the propensity for chipping, and to show the thermal residual stress resistance of the structure. Two different thickness ratios of 1:1and 1:2 mm, either rapidly or slowly cooled from sintering temperature to Tg were tested. The results demonstrated that the tested VITA VM 9 veneering ceramic and VITA In-Ceram combination had a lowest thermal shock resistance of 120 oC, with no significant differences emerging between the groups (P0.05). In addition, 100% of the samples failed cohesively and no delamination were identified. The tested system showed adequate thermal shock resistance, however with the most failed samples showed horizontal crack propagation that probably driven by compressive stresses provides a motive toward investigating a perfect TEC matching concept between the core and the veneering ceramic. 88 pp. Englisch.
2
9783330967465 - Fatien Fadilaldin: Thermal compatibility evaluation of veneering ceramic over zirconia
Fatien Fadilaldin

Thermal compatibility evaluation of veneering ceramic over zirconia (2017)

Lieferung erfolgt aus/von: Deutschland DE PB NW

ISBN: 9783330967465 bzw. 3330967463, in Deutsch, 88 Seiten, Noor Publishing, Taschenbuch, neu.

Fr. 48.96 ( 49.90)¹
versandkostenfrei, unverbindlich
Lieferung aus: Deutschland, Versandkosten nach: Deutschland, Versandkostenfrei.
Von Händler/Antiquariat, Buchhandlung Hoffmann, [3174608].
Neuware - The residual stresses generated during manufacturing of zirconia prostheses is the origin of unstable chipping observed clinically. The aim of this study was to analyzing the influence of porcelain thickness and the implemented cooling protocol on the magnitude of the developed residual stresses. 60 rectangular bilayered plates and thermal shock test were used to investigate the propensity for chipping, and to show the thermal residual stress resistance of the structure. Two different thickness ratios of 1:1and 1:2 mm, either rapidly or slowly cooled from sintering temperature to Tg were tested. The results demonstrated that the tested VITA VM 9 veneering ceramic and VITA In-Ceram combination had a lowest thermal shock resistance of 120 oC, with no significant differences emerging between the groups (P0.05). In addition, 100% of the samples failed cohesively and no delamination were identified. The tested system showed adequate thermal shock resistance, however with the most failed samples showed horizontal crack propagation that probably driven by compressive stresses provides a motive toward investigating a perfect TEC matching concept between the core and the veneering ceramic. 06.06.2017, Taschenbuch, Neuware, 220x150x5 mm, 147g, 88, Internationaler Versand, offene Rechnung (Vorkasse vorbehalten), sofortueberweisung.de, Selbstabholung und Barzahlung, Skrill/Moneybookers, PayPal, Lastschrift, Banküberweisung.
3
9783330967465 - Fatien Fadilaldin: Thermal compatibility evaluation of veneering ceramic over zirconia
Symbolbild
Fatien Fadilaldin

Thermal compatibility evaluation of veneering ceramic over zirconia

Lieferung erfolgt aus/von: Deutschland DE NW

ISBN: 9783330967465 bzw. 3330967463, in Deutsch, neu.

Fr. 46.06 ( 46.95)¹
versandkostenfrei, unverbindlich
Lieferung aus: Deutschland, Lieferzeit: 6 Tage.
The residual stresses generated during manufacturing of zirconia prostheses is the origin of unstable chipping observed clinically. The aim of this study was to analyzing the influence of porcelain thickness and the implemented cooling protocol on the magnitude of the developed residual stresses. 60 rectangular bilayered plates and thermal shock test were used to investigate the propensity for chipping, and to show the thermal residual stress resistance of the structure. Two different thickness ratios of 1:1and 1:2 mm, either rapidly or slowly cooled from sintering temperature to Tg were tested. The results demonstrated that the tested VITA VM 9 veneering ceramic and VITA In-Ceram combination had a lowest thermal shock resistance of 120 oC, with no significant differences emerging between the groups (P0.05). In addition, 100% of the samples failed cohesively and no delamination were identified. The tested system showed adequate thermal shock resistance, however with the most failed samples showed horizontal crack propagation that probably driven by compressive stresses provides a motive toward investigating a perfect TEC matching concept between the core and the veneering ceramic.
4
9783330967465 - Fadilaldin, Fatien: Thermal compatibility evaluation of veneering ceramic over zirconia
Symbolbild
Fadilaldin, Fatien

Thermal compatibility evaluation of veneering ceramic over zirconia

Lieferung erfolgt aus/von: Deutschland DE PB NW

ISBN: 9783330967465 bzw. 3330967463, in Deutsch, Taschenbuch, neu.

Fr. 48.27 ( 49.20)¹
versandkostenfrei, unverbindlich
Lieferung aus: Deutschland, Versandkostenfrei.
Von Händler/Antiquariat, European-Media-Service Mannheim [1048135], Mannheim, Germany.
Publisher/Verlag: Noor Publishing | Evaluation of Thermal Compatibility of VITA VM 9 Veneering Ceramic Over VITA In-Ceram Zirconia Framework | The residual stresses generated during manufacturing of zirconia prostheses is the origin of unstable chipping observed clinically. The aim of this study was to analyzing the influence of porcelain thickness and the implemented cooling protocol on the magnitude of the developed residual stresses. 60 rectangular bilayered plates and thermal shock test were used to investigate the propensity for chipping, and to show the thermal residual stress resistance of the structure. Two different thickness ratios of 1:1and 1:2 mm, either rapidly or slowly cooled from sintering temperature to Tg were tested. The results demonstrated that the tested VITA VM 9 veneering ceramic and VITA In-Ceram combination had a lowest thermal shock resistance of 120 oC, with no significant differences emerging between the groups (P0.05). In addition, 100% of the samples failed cohesively and no delamination were identified. The tested system showed adequate thermal shock resistance, however with the most failed samples showed horizontal crack propagation that probably driven by compressive stresses provides a motive toward investigating a perfect TEC matching concept between the core and the veneering ceramic. | Format: Paperback | Language/Sprache: english | 88 pp.
5
9783330967465 - Fatien Fadilaldin: Thermal compatibility evaluation of veneering ceramic over zirconia: Evaluation of Thermal Compatibility of VITA VM 9 Veneering Ceramic Over VITA In-Ceram Zirconia Framework
Fatien Fadilaldin

Thermal compatibility evaluation of veneering ceramic over zirconia: Evaluation of Thermal Compatibility of VITA VM 9 Veneering Ceramic Over VITA In-Ceram Zirconia Framework (2017)

Lieferung erfolgt aus/von: Deutschland EN PB NW

ISBN: 9783330967465 bzw. 3330967463, in Englisch, 88 Seiten, Noor Publishing, Taschenbuch, neu.

Fr. 43.12 ( 43.95)¹
versandkostenfrei, unverbindlich
Lieferung aus: Deutschland, Versandfertig in 1 - 2 Werktagen, Versandkostenfrei.
Von Händler/Antiquariat, dodax-shop-eu.
Die Beschreibung dieses Angebotes ist von geringer Qualität oder in einer Fremdsprache. Trotzdem anzeigen
Lade…